Fluorocarbon paint special intermediate paint D-FC-301
Category:
Exterior Wall Latex Paint Series
Tel:
E-mail:
Introduction
Product Description
Made from imported high-weather-resistant acrylic resin as the main base material, combined with titanium white and other pigment fillers, additives, and solvents. This product is packaged in A and B two-component sets.
Product Features
This product has a tough film, good adhesion, high hardness, and good sanding properties, which can improve the filling properties of the primer and the adhesion between the primer and the topcoat.
Mainly used for mid-coating of automobiles, trains, bridges, building exteriors, steel structures, etc. It can be used on cathodic electrophoretic primers, amine-cured epoxy primers, and unsaturated polyester putties, and is also suitable for coating materials such as properly treated steel, aluminum alloys, ABS plastics, wood, and ceramics, enhancing the fullness of the topcoat and improving its decorative effect.
Physical Parameters
Solid Content: ≥50%
Density: (1.10~1.35) grams per milliliter.
Fineness: (Component A) ≤30 microns.
Drying Time: Surface dry in 30 minutes, fully dry in 24 hours, completely cured in 7 days, at a temperature of (23±2) °C. Theoretical coverage rate: (8~10) square meters/kilogram (dry film thickness 30 microns). Mixing ratio: Component A: Component B = 1:0.005 (by weight).
Usable Period: Use within 8 hours after mixing. Temperature (23±2) °C.
Storage: Store in a cool, dry place, effective storage period for Component A is one year, for Component B is six months. Packaging: 24 kilograms/set.
Construction Instructions
1. Ensure the surface of the object to be coated is free of oil, dust, dry, and protected from other paint mist contamination.
2. After the primer is fully dry, it must be sanded clean before spraying this paint. This coating is mixed in the ratio of Component A: Component B = 1:0.005, and must be thoroughly stirred and accurately weighed during use, otherwise it will affect the coating performance.
3. Use the matching special thinner D-X-2.
4. Mix in the ratio of Component A: Component B = 23:1 (by weight) until uniform. Then slowly dilute with thinner to the construction viscosity while stirring, generally 18~25 seconds (using a No. 4 cup), let it sit for 20~30 minutes to fully mature, and after bubbles disappear, it can be applied. Filter with a 200 mesh copper wire screen before application.
5. This coating can be brushed or sprayed. The brushing viscosity is slightly higher, and for spraying, it depends on the type of spray gun, the area to be coated, and the viscosity of the paint, with spraying pressure between 3.5~6.0 atmospheres.
6. The usable period of this two-component coating after mixing is 6~8 hours, prepare as needed to avoid waste.
7. After spraying the first coat, wait 8~10 minutes before spraying the second coat, which can be slightly lower in viscosity than the first.
Safety and Environmental Instructions
Avoid contact with skin and eyes; if contact occurs, rinse with clean water. The site must be well-ventilated. The paint contains flammable components, please keep away from sparks and prohibit smoking in nearby areas. Follow all health and safety regulations on site.
Key words:
Fluorocarbon paint special intermediate paint D-FC-301
Previous Page:
Message
Related Products
Message
* Note: Make sure you fill in the information accurately and keep the communication open, we will contact you as soon as possible.
Contact Us
No.19, Jingkai Second Avenue, Zhengzhou Economic and Technological Development Zone, China
Telephone
Page Copyright©Henan Dejiali Technology Group Co., Ltd.
Powered by :www.300.cn Supported IPV6 Privacy Agreement